ATLAS ANGUCEL ES-100

ATLAS ANGUCEL ES-100

sealing admixture for production of ready-mix and vibropressed concrete, for decreasing capillary pulling and reducing risk of occurring efflorescence

ATLAS ANGUCEL ES-100

Product description

Sealing admixture designed for:
- Production of ready-mix concrete with reduced capillary pulling and absorptivity,
- Production of vibropressed concrete with low required absorptivity and reduced capillary pulling e.g. concrete paving, plates, borders – admixture can be dosed to the construction and surface-finish layer,
- Production of coloured concrete with reduced risk of occurring lime efflorescence.

Main properties

    - Efficiently hydrophobizing capillary walls to prevent from capillary pulling and washing off soluble salts which results in lower risk of occurring lime efflorescence - Permanently hydrophobizing and protecting from weather conditions impact due to chemical reaction between cement and admixture active substances - Improves concrete staining due to reduction of efflorescence - Enables to obtain “drop effect” on hydrophobized surfaces - Increases concrete resistance for de-icing agents and freeze-thaw cycles - Decreases risk of algae and mosses overgrowth on building materials - Decreases concrete absorptivity - For concrete exposed to impact of water under pressure it is recommended to use additionally water-reducing admixtures to reduce water-cement coefficient, e.g. from DURUFLOW series

Main parameters

    Base: Aqueous emulsion of silanes/siloxanes Form: White liquid Density: 0.98 — 1.02 g/cm3 pH rate: 7.0 — 9.0

USE

Go top
·          Production of ready-mix concrete with reduced capillary pulling and absorptivity
·          Production of vibropressed concrete with low required absorptivity and reduced capillary pulling e.g. concrete paving, plates, borders – admixture can be dosed to the construction and surface-finish layer
·          Production of coloured concrete with reduced risk of occurring lime efflorescence

PROPERTIES

Go top
·          Efficiently hydrophobizing capillary walls to prevent from capillary pulling and washing off soluble salts which results in lower risk of occurring lime efflorescence
·          Permanently hydrophobizing and protecting from weather conditions impact due to chemical reaction between cement and admixture active substances
·          Improves concrete staining due to reduction of efflorescence
·          Enables to obtain “drop effect” on hydrophobized surfaces
·          Increases concrete resistance for de-icing agents and freeze-thaw cycles
·          Decreases risk of algae and mosses overgrowth on building materials
·          Decreases concrete absorptivity
·          For concrete exposed to impact of water under pressure it is recommended to use additionally water-reducing admixtures to reduce water-cement coefficient, e.g. from DURUFLOW series

TECHNICAL REQUIREMENTS

Go top
Base
Aqueous emulsion of silanes/siloxanes
Form
White liquid
Density
0.98 — 1.02 g/cm3
pH rate
7.0 — 9.0

DOSAGE

Go top
Recommended                  0.2 – 1.5 % of cement mass
Optimum in ready-mix concrete
                                      0.8 – 1.2 % of cement mass
Optimum in vibropressed two-layer elements
Finishing coat                   0.5 – 1.0 % of cement mass
Construction layer
-without plasticizers           0.4 – 0.8 % of cement mass
-with plasticizers               0.25 – 0.5 % of cement mass
 
Dosage depends on, i.e. binder type, ambient temperature, aggregate grading curve.

SHELF LIFE

Go top
12 months from the production date shown on the packaging. Production date and batch number are placed on the packaging.

STORAGE AND TRANSPORT

Go top
Keep in original, undamaged containers in temperature from +5°C up to +30°C. Protect from freezing and intense sunlight. Mix the product after prolonged storage.

APPLICATION

Go top
ATLAS ANGUCEL ES 100 admixture should be added as the final compound of cement mixture. Too early addition can result in reduction of concrete hydrophobization level. Mixing time must be sufficient to obtain homogenous concrete mix and should be determined by trials.
After forming, concrete should be properly maintained in order to reach the designed parameters.

REQUIREMENTS

Go top
Product compliant with EN 934-2 + A1:2012
Product holds Declaration of Performance no 032/D/CPR and Factory Production Control Certificate no 1488-CPR-0396/Z issued by the Building Research Institute in Warsaw.
17
032/D/CPR
1488-CPR-0396/Z
PN-EN 934-2+A1:2012
 
ATLAS ANGUCEL ES-100
 
CE
1488
EN 934-2 T9
Sealing concrete admixture
Chloride ions content
Maximum 0.1%
(chloride-free admixture)
Alkaline content
Maximum 0.5%
Capillary absorption
After 7 days of maturing, tested for 7 days for mortar with ≤ 50% control mortar
After 90 days of maturing, tested for 28 days for mortar with admixture ≤ 60% control mortar
Compressive strength
After 28 days concrete tested ≥ 85% control sample
Air content
In tested mixture ≤ 2% volume above content in control sample
Corrosive effect
Does not cause corrosive effect, tested according to EN 480-14:2008
Dangerous compounds
See: Safety Data Sheet

PACKAGING

Go top
Barrel               200 kg, 220 kg
IBC                   1000 kg

REMARKS

Go top
Detailed information on health, safety and ecology
is available in the Safety Data Sheet and on the label.
The above information constitutes basic guidelines for the application of the product and does not release the user from the obligation of carrying out works according to engineering principles and OHS regulations. At the time of publication of this product data sheet all previous ones become void.
Date of update: 2017.03.16
Go top
ATLAS ANGUCEL ES-100
ATLAS ANGUCEL ES-100
sealing admixture for production of ready-mix and vibropressed concrete, for decreasing capillary pulling and reducing risk of occurring efflorescence