ATLAS ZŁOTY WIEK TG

ATLAS ZŁOTY WIEK TG

white renovation surface finishing coat

ATLAS ZŁOTY WIEK TG

Product description

For execution of thin-coat surface finish on typical mineral substrates like concrete, aerated concrete, brick and cement, gypsum and lime plasters.
For smoothing the surface of casted sculptures and architectural elements.
White – mortar based on white Portland cement.

Main properties

    Main parameters

    • layer thickness: from 1 to 5 mm
    • waterproof
    • consumption: up to 1.5 kg / 1 m²/ 1 mm layer thickness

    USE & PROPERTIES

    Go top

    ·          for execution of thin-coat surface finish on typical mineral substrates like concrete, aerated concrete, brick and cement, gypsum and lime plasters

    ·          for smoothing the surface of casted sculptures and architectural elements

    ·          white – mortar based on white Portland cement

    ·          based on dolomite flour of grain size of up to 0.1 mm – allows achieving ideally smooth surfaces

    ·          layer thickness between 1 and 5 mm

    ·          for indoor and outdoor application

    ·          waterproof

    ·          frost resistant

    SUBSTRATE PREPARATION

    Go top

    The method of surface cleaning must be individually adjusted for each object, depending on the strength and condition of the substrate material and its historic value. The substrate must be sound, free from dust, dirt, efflorescence, remains of painting coats. Hammer off poorly adhering pieces of the surface and remove loose or weak parts with steel brush. Directly before the application of plaster, wet the surface with water.

    APPLICATION

    Go top

    Pour the dry mix from the bag into a clean container with the suitable amount of water (recommended proportions: 8.5 l/25 kg) and mix mechanically until homogenous, lump free and without separating liquid. The mortar is ready to use after ca. 5 minutes and remixing. Apply the mortar in an even layer upon the substrate with a stainless steel float, pressing strongly against the substrate. The surface can be finished by grinding or light float finishing with a felt float. Mortar open time (between the application of the mortar and floating) depends on the substrate absorptivity, the ambient temperature and the consistency of the mortar. Protect the surface against excessive drying during the application of the material and its setting.

    REMARKS

    Go top

    ·          The above information constitutes basic guidelines for the application of the product and does not release the user from the obligation of carrying out works according to engineering principles and OHS regulations.

    ·          The tools must be cleaned with clean water directly after use. Difficult to remove residues of the set adhesive can be removed with the ATLAS SZOP agent.

    ·          The shelf life of the product is 12 months from the production date shown on the packaging. The mortar must be transported and stored in tightly sealed bags, in dry conditions (most preferably on pallets).

    ·          Irritant – contains cement. Risk of serious damage to the eyes. Can trigger allergic reaction on contact with skin. Keep out of the reach of children. Do not inhale the dust. Rinse contaminated eyes with large amounts of water and seek doctor’s assistance. Wear appropriate protective clothing, protective gloves and goggles or face protection. In case of ingestion immediately seek medical advice – show the packaging or label.

    TECHNICAL DATA

    Go top

    ATLAS GOLDEN AGE TG is a factory made dry mix manufactured on the basis of the highest quality mineral binder (cement and lime), dolomite fillers and improvers. The product conforms to PN-EN 998-1 standard. EC Declaration of Performance No. AZW TG/CPR.

    Mixing proportions: water/dry mix
    8.5 l/25 kg
    Pot life
    ca. 2 hours
    Open time
    ca. 15 minutes
    Consumption
    up to 1.5 kg of mortar for 1 m²

    at 1 mm layer thickness

    Mortar preparation temperature,

    substrate and ambient temperature during work

    from +5°C to +25°C
    Min. / max. coat thickness
    1 mm / 5 mm
    Available packaging
    paper bags of 25 kg

    Content of soluble chromium (VI) in ready-to-use mix

    ≤ 0.0002%
     
     

    Factory made plastering mix of specified properties,

    single-coat (OC), suitable for indoor and outdoor use

    CE 13
    Reaction to fire - class
    A1
    Adhesion
    ≥ 0.5 N / mm² - FP:B
    Compressive strength
    1.5 – 5.0 N/mm²
    Water absorption
    ≤ 0.4 kg / m² min0,5
    Water filtration examined
    after required ageing cycles [ml/cm² after 48 hours]
    ≤ 1
    Water vapour permeability coefficient μ
    15/35
    Thermal conductivity coefficient
    (average tabular value P=50%)
    0.83 W / mK (λ10,dry)
    Gross dry density
    ≤ 1800 kg/m³
    Durability.
    Mass decrement after freeze-thaw cycles
    < 3%
    Durability.

    Compressive strength decrease after freeze-thaw cycles

    < 10%